Huitian® 7262 is a one-component thread-locking anaerobic adhesive that
features thixotropy, medium-high strength, and excellent resistance
against fluid. The product cures when confined in the absence of
air between close-fitting metal surfaces.
Typical Application
Permanent locking of thread-locking below M20 can be widely used
for locking and sealing parts with large force.
Red Screw Thread Locking Adhesive 7262 replacing Loctite 262 for under M20 thread locker
Properties before curing
Typical value Range
Appearance Red liquid
Chemical type Methacrylate
Viscosity (mPa·s)
(GB/T2794-1995)
Brookfield RVT
3#spindle 2.5rpm 5,000~8,500 thixotropy
20 rpm 1,800~2,400 thixotropy
Density (g/cm3) 1.10 1.00-1.15
(GB/T13354-1992)
Flash point (℃) ＞93
(SH/T0733-2004)
Max filling gaps (mm) 0.13
Fixture time (min) ≤20
Properties after curing
Curing time at RT (h) 24
Breakaway torque (N·m) 22 14.1~28.2
Carbon steel natural color bolt (GB/T18747.1-2002)
Average dismounting torque (N·m) 30 16.9~33.9
Carbon steel natural color bolt (GB/T18747.1-2002)
Working temperature (℃) -50~150
Chemical/solvent resistance
Aged under conditions indicated and tested @ 22°C
Solvent Temperature (℃) % of initial strength
100h 500h 1000h 5000h
Engine oil 125 90 80 75 75
Leaded petrol 22 95 90 90 90
Brake fluid 22 100 100 100 100
Ethanol 22 90 90 75 75
Acetone 22 85 85 80 80
Water/glycol 87 100 70 65 60
(50%/50%)
Directions for use
Clean-up: For best results, clean all surfaces (external and internal) with
a Huitian 7755 cleaning solvent and allow to dry.
Gluing: Apply glue evenly to the thread engagement area, with sufficient
glue to fill the thread gap, and tighten in one pass as required by
the specification. Curing speed slows down as the gap increases If
the cure speed is too slow, spray all threads with Activator 7769
and allow to dry.
Assembly: Shake the product thoroughly before use. To ensure that the system
achieves maximum performance, the recommended curing time is 24
hours or more to ensure that the adhesive layer is fully cured.
Cautions
Not suitable for use on plastic parts, not suitable for use in pure
oxygen and oxygen-rich systems, and not for sealing chlorine or
other strong oxidizing substances.
Store unused glue in a sealed container for next use. Contaminated
glue should not be refilled into the original bottle as this may
affect the performance of the remaining glue.
This product contains acrylic and methacrylate substances which are
irritating to the skin and eyes. Recommended for use in a
ventilated area. In case of accidental contact with eyes and skin,
rinse immediately with water.
Keep away from children for storage.
For safe handling information on this product, consult the Safety
Data Sheet (SDS).
Packing specification
Order code: 726201, 50ml/tube, 10 pcs/carton, 80 pcs/box
726203, 250ml/bottle, 10 pcs/carton
Storage
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than
28 °C can adversely affect product properties.
Shelf life is 18 months
We can also make:
1. Low strength & thixotropic thread locker
2. Middle strength & thixotropic thread locker
3. High strength & oil resistant thread locker
4. High strength & chemical resistant thread locker
5. High strength & thixotropic thread locker
6. High strength & high viscosity thread locker
7. High strength & middle viscosity thread locker
8. High-strength & high-temperature resistant thread locker
9. High strength & fast osmotic thread locker
Performance of thread locker and sealant anaerobic
adhesive/pre-coated thread locker and sealant anaerobic adhesive
| Product name | Appearance | Viscosity mPa·s GB/T2794 | Density g/cm³ GB/U3354 | Maximum filling gap mm | Failure moment N·m GB/T18747.1 | Average disassembly torque N·m GB/T18747.1 | Initial curing time min | Full curing time h | Working temperature ℃ |
| 7242 | Blue | 800 -1,600 Thixotropy** | 1.0 | 0.13 | 12 | 5 | <20 | 24 | -50-150 |
| 7243 | Blue | 1,600 -1,900 Thixotropy** | 1.08 | 0.13 | 20 | 10 | <20 | 24 | -50-150 |
| 7262 | Red | 1,800 -2,400 Thixotropy** | 1.1 | 0.13 | 22 | 32 | <20 | 24 | -50-150 |
| 7263 | Red | 800-1,200* | 1.1 | 0.13 | 30 | 25 | <45 | 24 | -50-180 |
| 7271 | Red | 450~550 * | 1.1 | 0.13 | 25 | 29 | <20 | 24 | -50-150 |
| 7272 | Red | 4,000-10,000 Thixotropy*** | 1.11 | 0.3 | 23 | 25 | <60 | 24 | -50-230 |
| 7277 | Red | 6,000- 9,000*** | 1.12 | 0.25 | 32 | 31 | <20 | 24 | -50-150 |
| 7204 | Red | 7,000-15,000 Thixotropy**** | 1.1 | N/A | 22 | N/A | <5 | 72 | -50-150 |
| 7204D | Red | 9,000~15,000 Thixotropy | 1.1 | N/A | 25 | N/A | ≤5 | 72 | -50~150 |
| 7213 | Red, yellow, blue, orange, rose red, blue-green | 1,600~3,000 | 1.05 | N/A | 20 | N/A | ≤5 | 72 | -50~150 |
| 7215 | Rose red, yellow, blue-green | 1,600~3,000 | 1.05 | N/A | 20 | N/A | ≤5 | 72 | -50~150 |
Note: *Viscosity - measured at Brookfield RVF 20rpm: *2 # rotor **3
# rotor ***4 # rotor ****5 # rotor
Our Advantages:
1. Listed company in China (stock code: 300041)
2. Famous Trademark of China
3. Fast Delivery
4. OEM services/small orders are welcome